Triazole Based Cross-linked Polyimide as Gate Dielectric for Low Temperature Processable Organic Thin Film Transistor
발표자
()
초록
내용
Organic thin film transistors (OTFTs) for flexible devices require low temperature processing. We report a new cross-linker, 1,3,5-tris(2-propynyloxy)benzene (TYB), which can be cross-linkable at very low temperature 100 oC. Firstly, azide functionalized soluble polyimide is synthesized, and then cross-linking occurs through azide-alkyne cycloaddition reaction with a 1,3,5-tris(2-propynyloxy)benzene (TYB) cross-linker. The metal-insulator-metal (MIM) devices show that they show good leakage current density (3.09ⅹ10-8 A/cm2 at 1 MV/cm) and dielectric constant (3.42) even when cross-linked at very low temperature. Also, it shows good mobility (0.404 cm2/Vs) and on/off ratio (1.25ⅹ105) through the pentacene TFT. Detailed polyimide synthesis method and film fabrication condition will be presented.